″RP120L″ is a low sealing temperature polypropylene resin. The product is designed for BOPP films and is formulated with standard processing stabilization and is calcium stearate free.
Value | Unit | Method | |
Physical | |||
Melt Flow Rate (230 °C, 2.16 kg) | 6.0 | g/10min | ASTM D1238 |
Density | 0.9 | g/cm3 | ASTM D1505 |
Mechanical | |||
Flexural Modulus | 650 | MPa | ASTM D790 |
Tensile Strength at Yield | 22 | MPa | ASTM D638 |
Tensile Elongation at Yield | 12 | % | ASTM D638 |
Izod Impact Strength (notched) at 23 °C | 80 | J/m | ASTM D256 |
Thermal | |||
Melting Temperature (DSC) | 136 | °C | ASTM D3417 |
Vicat softening point (10N) | 118 | °C | ASTM D1525 |
H.D.T. (0.45 MPa) | 65 | °C | ASTM D648 |
Accelerated oven ageing in air at 150 °C | 300 | hours | ASTM D3012 |
Optical | |||
Haze (1 mm) | 1.0 | % | ASTM D1003 |
Gloss | 85 | —- | ASTM D2543 |